The claimed characteristics of the materials sold by us may differ only for the better
Materials for waterproofing industrial seams
Bitumen-polymer hermetic №42 (BP)
Usage: Airport, Parking of cars, Reconstruction of roads, Strengthening of asphalt-concrete seam, Waterproofing of bridges, Waterproofing of expansion joints, Waterproofing of industrial seams, Waterproofing of road surfaces
Bitumen-polymer sealant Technonikol No. 42 is a one-component material consisting of oil bitumen, modified with rubber and technological additives. Available in three versions, depending on climatic zones: BP-G25, BP-G35, BP-G50. A sealant is used in road construction to seal expansion joints in highways, runways of aerodromes and highways.
The name of indicators Unit. measurements Value Test method BP-G25 BP-G35 BP-G50 Softening temperature, not lower than 0С 90 90 90 Flexibility on the rod Æ 20 mm, not higher 0С -25 -35 -50 Relative elongation at the moment of rupture, not less than at -20 ° C % 75 75 75 -||- Temperature of stickiness, not less than 0С 50 50 50 -||- Stamina, number of cycles, no less than – 30000 30000 30000 -||- Water absorption, not more than % 0,2 0,2 0,2 -||- Change in properties under UV irradiation, not more than ч 1000 1000 1000 -||- Bituminous polymer polymeric Albizol (BP)
Usage: Airport, Parking of cars, Reconstruction of roads, Strengthening of asphalt-concrete seam, Waterproofing of bridges, Waterproofing of expansion joints, Waterproofing of industrial seams, Waterproofing of road surfaces
Bituminous polymer polymeric Albizol (BP) – produced at the Kostroma waterproofing materials plant, is an improved and more inexpensive modification of the bituminous polymer sealant Technonikol (higher adhesion, higher softening point, more UV stabilizers). It is used to seal expansion joints, to rehabilitate temperature and strength cracks in cement concrete, asphalt and concrete and polymer-concrete coatings of roads, bridges, aerodromes (there is an experience of Albizol application both at civil airfields and military ones)
The name of indicators Unit. measurements Value BP-G25 BP-G35 BP-G50 Softening temperature, not lower than 0С 100 100 100 Flexibility on the rod Æ 20 mm, not higher 0С -25 -35 -50 Relative elongation at the moment of rupture, not less than at -20 ° C % 75 150 200 Temperature of stickiness, not less than 0С 50 50 50 Stamina, number of cycles, no less than – 30000 30000 30000 Water absorption, not more than % 0,5 0,5 0,5 Change in properties under UV irradiation, not more than h 1000 1000 1000 Mastic bitumen-polymer MKTN
Usage: Mastic roofs, Parking of cars, Strengthening of asphalt-concrete seam, Waterproofing of foundations, Waterproofing of industrial seams, Waterproofing of road surfaces
The peculiarity of bitumen-polymer mastic MKTN is in the widest temperature range of its application (from -200 to +300 degrees). The usage regulations developed by the manufacturer for this mastic include: the device and repair of all types of roofs (pitched and flat, in combination with rolled waterproofing materials, glass fabrics and without them), for waterproofing of buried objects (foundations, cellars, piles, etc.)
Mastic bitumen-rubber “Stroymast”
Usage: Mastic roofs, Parking of cars, Strengthening of asphalt-concrete seam, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams
Mastic bituminous rubber “Stroymast” is designed for any waterproofing work, produced outdoors. The composition of the mastic is SBS-modified bitumen, technological additives, mineral fillers, as well as an organic solvent (the presence of which excludes the use of mastic for internal waterproofing operations). It is an inexpensive equivalent of Tekhnonikol mastic # 20.
Mastic bitumen-rubber № 20
Usage: Inversion roofs, Mastic roofs, Parking of cars, Strengthening of asphalt-concrete seam, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams
Mastic bituminous-rubber № 20 is designed for any waterproofing work, produced outdoors. The composition of the mastic is SBS-modified bitumen, technological additives, mineral fillers, as well as an organic solvent (the presence of which excludes the use of mastic for internal waterproofing operations). A special feature of the mastic is its high hardness when drying, as well as a high temperature range of application (can be stacked at -20 to +40 degrees)
Mastic Hot Bituminous Rubber MBR
Usage: Parking of cars, Strengthening of asphalt-concrete seam, Waterproofing of bridges, Waterproofing of expansion joints, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams, Waterproofing of road surfaces
Roofing mastic of hot application Eureka No. 41 is designed for effective repair and flat roofing, but can also be used for waterproofing steel structures, concrete blocks, columns, concrete building blocks and pipelines. The use of hot waterproof mastics is more effective and durable than the use of cold mastics because of the greater liquidity of the material
Indicator name Unit. measurements Normative value MBR-65 MBR-75 MBR-90 MBR-100 Softening temperature according to the KiS method, not less than оС 65 75 90 100 Depth of penetration of the needle at 25 оС, not less than 0,1 mm 40 30 20 15 -||- Растяжимость при 25 оС, не менее cm 4 4 3 2 -||- Водонасыщение за 24 ч, не более % 0,2 0,2 0,2 0,2 Application temperature, within 0С +5 to -30
+15 to -15
+35 to -5
От +40 to -5 – Mastic hot bituminous-rubber MBR 75 ZKM
Usage: Parking of cars, Strengthening of asphalt-concrete seam, Waterproofing of bridges, Waterproofing of expansion joints, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams, Waterproofing of road surfaces
Hot bitumen – rubber mastic consists of petroleum bitumen, rubber crumb and plasticizer with a softening temperature of 75 grains, produced at the Kostroma waterproofing materials plant, is an inexpensive analogue of MBM mastic from Technonikol. It is intended for the device of waterproofing and anticorrosion protection of underground pipelines, and also for sealing of cracks and seams on flat roofs. Available in several modifications, differing in density and strength characteristics.
Indicator name Unit. measurements Normative value MBR-75 Softening temperature according to the KiS method, not less than оС 75 Depth of penetration of the needle at 25 оС, not less than 0,1 mm 30 Extensibility at 25 оС, not less than см 4 Water saturation for 24 hours, no more than % 0,2 Application temperature, within 0С От +15 до -15
Mastic protective polymeric aluminum №57
Usage: Mastic roofs, Parking of cars, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams, Waterproofing of road surfaces
Tekhnonikol waterproofing mastic # 24 is designed for waterproofing concrete structures, concrete products, wood and other building structures that are buried and are in permanent or permanent contact with water. It is important to note that this mastic is not roofing (ie does not contain ultraviolet stabilizers, as well as rubber impurities), that is, the use of MGTN No. 24 for repair and roofing is highly discouraged.
Mastics roofing waterproofing № 31
Использование: Inversion roofs, Mastic roofs, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams
Mastic roofing emulsion No. 31 consists of petroleum bitumen, modified with artificial rubber, technological additives and mineral fillers and does not contain organic solvents, which also allows for the use of mastic for internal waterproofing works. In addition, Mastic No. 31 has one of the highest adhesion values with concrete in the whole line of Tekhnonikol mastics.
Mastics roofing waterproofing №21 (Technomast)
Usage: Mastic roofs, Waterproofing of flat roofs, Waterproofing of foundations, Waterproofing of industrial seams
Mastics roofing waterproofing – finished mastic cold application on the basis of bitumen, in the composition of mastic there are technological additives: artificial rubber, mineral fillers, organic solvent, providing high adhesion to virtually any substrate. An important difference between roofing mastics and waterproofing mastics is the presence of ultraviolet stabilizers.